Testing of Bolts, Screws and Studs to DIN EN ISO 898-1, ASTM F606-1, DIN EN ISO 3506-1

Testing of bolts, screws and studs to DIN EN ISO 898-1, ASTM F606-1, DIN EN ISO 3506-1 is used to determine mechanical properties such as tensile strength, offset yield, fracture elongation or hardness. 

As some of the most important fasteners, bolts, screws and studs are not only considered universally important in industry settings, but also for every day purposes. They are used in construction of complex machinery and equipment, as well as vehicles and buildings. Since mechanical stress is concentrated on these types of connection points, the integrity of fasteners is extremely important. Therefore bolts, screws and nuts are subject to strict safety requirements.

Broken threaded fastener

Property Classes

Property classes of bolts and screws are identified with two numbers separated by a dot. The number to the left of the dot is the tensile strength in MPa divided by 100. The number to the right of the dot indicates the tenfold of the yield point or offset yield ratio.

For example, a screw of property class 9.8 would have the following nominal values:

  • Nominal tensile strength: Rm = 9 × 100 MPa = 900 MPa
  • Yield point ratio: Re/Rm = 8 ÷ 10 = 0.8
  • Yield point: Re = 0.8 × 900 MPa = 720 MPa

The property class of a nut is identified with a single number, which corresponds to the highest property class of a screw with which the nut can be paired. A nut of property class 9 can be paired, for example, with a screw up to property class 9.8.

Terminology

In the different mechanical test methods a distinction is made between finished and full-size fasteners and between fasteners with full loading capacity and reduced loading capacity.

Finished fasteners are fasteners for which all manufacturing steps have been completed. So they are completely finished fasteners.

Full-size fasteners are finished fasteners on which the shank diameter is fully retained for tensile testing. They are also referred to as full shank fasteners. This designation excludes thin and expansion bolts and banjo bolts.

Fasteners with reduced loading capacity are usually not fully loadable due to their head geometry (so called weak-head screws), unlike screws of typical geometry of the same property class. Such screws are identified with a leading zero.

Tensile Test on Screws, Bolts and Studs

Threaded fasteners are selected very carefully with regard to their industrial application and are integrated carefully into the design. Accurate determination (via tensile tests) of the elastic tensile modulus and the limits of elastic loading is essential, since these values determine the limit forces required for a secure, reliable threaded connection.

All variations of the tensile test (Sections 9.1-5 and 9.7) must be performed according to ISO 6892-1, where the test speed shall not exceed 25 mm/min. In addition, the test speed shall not exceed 10 mm/min. in the determination of yield point or offset yield.

For full-size fasteners, the tests defined in sections 9.2 and 9.3 for the determination of offset yield, tensile strength and elongation after fracture may be combined in one tensile test.

Test fixture for tests on threaded fasteners
Specimen holders for testing of threaded fasteners to DIN EN ISO 898-1, ASTM F606-1, DIN EN ISO 3506-1

Proof Load Test on Threaded Fasteners

The proof load test (section 9.6) is a tensile test, that is only performed up to pure intended test load. The exact test load depends on the thread, diameter of the fastener and the property class. These are listed in a table in ISO 898-1.

When applying the test load, the test speed shall not exceed 3 mm/min. The load is held for 15 seconds and the fastener has passed the test if there is no resulting plastic elongation within the permissible measurement uncertainty of ±12.5 μm.

Test fixture for testing of threaded fasteners to DIN EN ISO 898-1, ASTM F606-1, DIN EN ISO 3506-1

Hardness Test on Threaded Fasteners

The methods to Vickers (ISO 6507-1), Brinell (ISO 6506-1) or Rockwell (ISO 6508-1) are permissible for the determination of hardness.

For hardness testing to Vickers a minimum load force of HV 10 applies. Hardness testing to Brinell is mainly performed with HBW 1/30 or HBW 2.5/187.5. For hardness testing to Rockwell, scale B (HRB) is used for fasteners of property class 4.6 - 6.8 and scale C (HRC) for property classes 8.8 - 12.9. In the event of arbitration, the Vickers hardness test shall be used as reference.

Hardness is either measured on the cross-section or on the surface. In the first case, a cross-section specimen is taken from the threaded area. Indentations are made near the fastener’s axis and the resulting hardness is also referred to as core hardness. When hardness is measured on the surface, the surface must be flat (e.g. on the head, on the end of the fastener or on the unthreaded shank) after removal of any coating.

In the retempering test Vickers hardness is measured before and after heat treatment. The reduction of hardness after retempering, if any, shall be less than 20 Vickers units.

In the decarburization and carburization test hardness is tested to Vickers with a test force of 2.942 N (HV 0.3) on a longitudinal section through the thread axis. The thread zone is measured on three defined points with different distances to the surface. Differences in measured values that are either too small or too large are an indication of decarburization or carburization.

Head Soundness Test on Threaded Fasteners

For the head soundness test, the bolt or screw is inserted into a pre-drilled solid block at an angle. The head of the fastener is bent at a defined angle with a striking motion, and no signs of cracking shall be visible after the test. This test is generally used when the tensile test under wedge loading cannot be carried out due to the too-short length of the fastener.

The Charpy impact test is only used in testing of fasteners, if it is required by a product standard or a corresponding agreement is made between the manufacturer and the customer.

Torsion Test on Fasteners

The torsion test is used to determine the breaking torque. The requirements and the method are described in ISO 898-7 (Torsional test and minimum torques for bolts and screws).

Charpy Impact Test on Fasteners

The purpose of the Charpy impact test is to determine the loading capacity of the fastener material at low temperature. Since a Charpy V-notch specimen has to be cut out of the fastener, the nominal diameter must be at least 16 mm. ISO 148-1 (Charpy pendulum impact test) describes the test method.